The Study of Effect of Applied Pressure on Microstructure and Actual Density for A380 Alloy by Use Squeeze Casting Process
الشريط الجانبي للمقالة
محتوى المقالة الرئيسي
الملخص
This present study shows, the effect of applying pressure at rang(10-84) MPa using squeeze casting process to improve the microstructure and actual density of Aluminum alloy A380 was studied.From fig(5) its clear that the microstructure of prepare casting samples consists of two phases of hard eutectic (Al-Si) and Primary α-Al. The effect of applying pressure leads to increase the surface fraction percentage of eutectic phase at (68-84) MPa, but the eutectic percentage was decreased at the same range the actual density was increased at (10,17,84) MP.
المقاييس
تفاصيل المقالة
هذا العمل مرخص بموجب Creative Commons Attribution 4.0 International License.
THIS IS AN OPEN ACCESS ARTICLE UNDER THE CC BY LICENSE http://creativecommons.org/licenses/by/4.0/
##plugins.generic.plaudit.displayName##
المراجع
Vijian P., Arunachalam V.P., “Modeling and multi-objective optimization of LM24 aluminum alloy squeeze cast process parameters using genetic algorithm” J. Mat. Proc. Tech., vol.186, 2007, pp. 82-86. DOI: https://doi.org/10.1016/j.jmatprotec.2006.12.019
Maleki A., Niroumand B., Shafyei A.,“Effects of squeeze casting parameters on density, macrostructure, and hardness of LM13 alloy” Mat.Sci.Eng., vol. A428, 2006, pp. 135-140. DOI: https://doi.org/10.1016/j.msea.2006.04.099
Hu H., “Squeeze casting of magnesium alloys and their composites” J. Mat. Sci., vol. 33, 1998, pp. 1579-1589.
Smillie M., “Casting and analysis of squeeze cast Aluminum silicon eutectic alloy” Ph.D. thesis, Department of Mechanical Engineering, University of Canterbury, Christchurch, New Zealand, 2006.
Yue T.M., “Squeeze casting of high- strength aluminum wrought alloAA7010” J. Mat. Proc. Tech., vol. 66,1997, pp. 179-185. DOI: https://doi.org/10.1016/S0924-0136(96)02516-2
Dionne S., “Influence of titanium diboride reinforcements on the microstructure, mechanical properties and fracture behavior of cast zinc aluminum composites” Ph.D. thesis, department des mines et metallurgy, Faculte des sciences et de genie, university laval, Quebec, CANADA, sept. 1999.
Hong C.P., Shen H.F., Cho I.S.,“Prevention of macrosegregation in squeeze casting of an Al-4.5wt Cu alloy” Met. Mat. Trans., vol. 29A, Jan. 1998, pp. 339-349. DOI: https://doi.org/10.1007/s11661-998-0185-z
Muhammed O.S., “Studying the parameters affecting the production of Al-alloy composite materials bu squeeze casting ” Ph.D. thesis, University Of Technology, Baghdad, .2008
M. A. Meyers, K.K. Chawala,”Mechanical Behavior of Metals”, Prentice – Hall, Inc., USA .1999, PP.249-252.
Qing Zhang, Mohsen Masoumi &Henry Hu,”Influence of Applied Pressure on Tensile Behaviour and Microstructure of Squeeze Cast Mg Alloy AM50 With Ca Addition”, J.of Materials Engineering and Performance, 2011. DOI: https://doi.org/10.1007/s11665-010-9810-2
Adam Equipment follows a policy of continuous improvement and reserves the right to change specifications without notice. ©January 2008.