Experimental Study for Some of the Mechanical and Physical Properties for the Binary Polymer of (Epoxy resin - Polyurethane)
الشريط الجانبي للمقالة
محتوى المقالة الرئيسي
الملخص
This study aimed to prepare a mixture of binary polymer composed of Epoxy resin and
Polyurethane Liquid Rubber, by ordinary mixing. Then, studying the mechanical properties
which are hardness, tensile strength, compressive strength, fluxral strength and finally impact
strength and also studying physical properties which are water absorption and thermal
conductivity for the mixture before and after submerging it with distilled water for different
durations. The base material was the epoxy resin (Quick Mast 105), with a hardener ratio of
(1:3), while the additive was the Polyurethane Liquid Rubber and a hardener ratio of (1:3), as
well. Furthermore, the weight ratio of the Polyurethane Liquid Rubber to the epoxy was 15% wt.
The results showed that the tensile and impact strengths and thermal conductivity, are
directly related with submerging duration from (0–28) day where it increase by 37.65%,
241.67%, 29.5% respectively, on the contrary to the hardness of the mixture, which decreases
by 7.35% with the duration length. The bending strength increases by 125% with the increase of
86 )93 -86( )2017( )2( مجلة تكريت للعلوم الهندسية 24the duration till it reaches a duration of 14 days, then it drops again with increase the duration of
28 days. It was found that the percentage of water absorption increased with increasing duration
of immersion (0–5) day even up to 1.65%. It was also found that the toughness of the dry
mixture is higher than the toughness of the mixture submerged with distilled water.
المقاييس
تفاصيل المقالة
هذا العمل مرخص بموجب Creative Commons Attribution 4.0 International License.
THIS IS AN OPEN ACCESS ARTICLE UNDER THE CC BY LICENSE http://creativecommons.org/licenses/by/4.0/
##plugins.generic.plaudit.displayName##
المراجع
- Al–Rawi KhR, Yosif RH, Najem TS.
Mechanical properties of epoxy–
polyurethane polymer blends. Um–Salama
Science Journal. 3(4); 2006: 637–642. DOI: https://doi.org/10.21123/bsj.3.4.637-642
-2 الراوي، خالد رشاد و سلمان، رفقة عامر، دراسة
Epoxy – بعض الخصائص الميكانيكية لمتراكب
مجلة جامعة النهرين للعلوم، المجلد 17 ، العدد ،MgO
.14 –10 :2014 ;1
-3 الراوي. خالد رشاد، جعفر، حارث إبراهيم، عبدالله،
هند وليد، دراسة خاصية الكلال لمتراكبات الايبوكسي
المدعمة بألياف الكفلر زجاج، مجلة ديالى للعلوم
.132 – 120 :2012 ; الصرفة، المجلد 8، العدد 3
-4 مكي، سمير عطا، احمد، عدي حميد، عبدالله،
مصطفى زيد، غني، بسمة علي، دراسة تأثير التدعيم
ودرجة الحرارة، في مقاومة الصدمة لخليط بوليمري،
، مجلة ابن الهيثم للعلوم الصرفة والتطبيقية، المجلد 25
.178 –169 :2012 ; العدد 3 DOI: https://doi.org/10.1632/prof.2012.2012.1.169
-5 عبد الحسين، هدى جبار، تأثير الغمر في المحاليل
الكيميائية على الخواص الميكانيكية والفيزيائية
لمتراكبات بوليمرية مدعمة بدقائق نانو الومينا، المجلة
:2015 ; العراقية للعلوم، المجلد 56 ، العدد 3
.1963 –
- Jawad MK. Investigation of the
compression and dielectric strength
properties for epoxy blends reinforced With
glass fibers. Journal of Al–Nahrain
University. 16(2); 2013;110–114. DOI: https://doi.org/10.22401/JNUS.16.2.16
- Fadhil BM and Ahmed PS. Improving
mechanical properties of epoxy by adding
multi–wall carbon nanotube. Journal of
Theoretical and Applied Mechanics. 54(2);
: 551–560.
- Hammood AS, Al–Waily M, Kamaz AA.
Effect of fiber orientation on fatigue of
glass–fiber reinforcement epoxy composite
material. The Iraqi Journal for Mechanical
and Material Engineering. 11(2); 2011:
–358.
- American Society for Testing and
Materials, ASTM D 570 – 98, Standard test
method for water absorption of plastics;
-10 صاحب ، مزهر علي، دراسة تأبير اختلال درجة
الحرارة، على بع الخصائص الميكانيكية والحرارية
لمتراكب من البولي اثيلين عالي الكثافة المدعم بألياف
الزجاج، مجلة جامعة النهرين للعلوم، المجلد 15 ، العدد
.21–11 :2012 ;3
- Alfalahi AH, Khalef EZ. Effect of
chemical solutions on physical properties of
(epoxy/Al2O3) composites. IOSR Journal of
Engineering. 05(04); 2015: 42 –46. DOI: https://doi.org/10.15623/ijret.2015.0405009
- American Society for Testing and
Materials, ASTM D 5930–01, Standard test
method for thermal conductivity of plastics
by means of a transient line–Source
Technique; 2009.
- American Society for Testing and
Materials, ASTM D 2240–00, Standard test
method for rubber property–Durometer
Hardness; 2009.
- American Society for Testing and
Materials. ASTM D 6110–04, Standard test
method for determining the charpy impact
resistance of notched specimens of
plastics; 2009.
- American Society for Testing and
Materials, ASTM D 790–03, Standard test
method for flexural properties of
unreinforced and reinforced plastics and
electrical insulating materials; 2009.
- American Society for Testing and
Materials, ASTM D 638–03, Standard test
method for tensile properties of plastics;
- Salman KD, Noori S. Abd alamer A,
Mahmmod LH. Studying the mechanical
properties of unsaturated polyesters–B4C
system. 14(1); 2014. DOI: https://doi.org/10.1016/S0262-1762(13)70353-5
- American Society for Testing and
Materials, ASTM D 695–02a, Standard test
method for compressive properties of rigid
plastics; 2009.
-19 حمد، محمد غازي. تأبير الماء على مقاومة الصدمة
لمتراكبات البولي استر غير المشبع المدعم بالالياف
الزجاجية، مجلة الانبار للعلوم الهندسية، المجلد 5، العدد
.294 – 279 :2012 ;2
- Ramires ML, Nieto de Castro VCA.
Standard reference for the thermal
conductivity of water. American Institute of
Physics and American Chemical Society;
:1377–1381.