vol24no4pa1

References

[1] Paul Whittaker. Powder metallurgy review Inovar Communications Ltd. 2012;1(1).
[2] Thanyaporn Yodkaew, Monnapas Morakotjinda, Nattaya Tosangthum, Rungthip Krataitong, Pisan Siriphol, Bhanu Vetynugul, Sainate Chakthin, Nuchthana Poolthong. Sintered Fe-Al2O3 and Fe-SiC composites. Journal of Metals, Materials and Minerals. 2008;18(1):57-61.
[3] Prabhu B, Suryanarayana C, An L, Vaidyantha R. Synthesis and characterization of high volume fraction Al-Al2O3 nanocomposite powders by high – energy milling. Material Science and Engineering. 2006;A425:192.
[4] وحيد، محمــد سعيد و مجيد، سديـــر موفــق. الخواص الميكانيكية لمتراكب ذو أساس من الألمنيوم. مجلة الهندسة والتكنولوجيا. 2009; 27(15):517.
[5] Michael Shur, Sergey Rumyantsv, Michael Levinshten. SiC materials and devices. World Scientific Publishing Co. Pte. Ltd. 2006;1.
[6] Gherad Pensl, Florin Ciobnu, Thomas Frank, Michael Kriger, Sergey Resganov, Frank Schmid, Michael Weidner. SiC material properties. International Journal of High Speed Electronics and Systems. 2005;15(4):705-745.

Tikrit Journal of Engineering Sciences (2017) 24(4) 1- 8

The Effect of Heat Treatment on the Composite Properties Based on Aluminum and Reinforcement Alumina and Silicon Carbide Prepared By Powder Metallurgy  Technique

Raed Najeeb Razooqi Najeeb Salman Abtan Hashim ShukorHamood
Mechanical Eng. Dept., Tikrit University, Iraq

Abstract

Adoption of powder metallurgy technique used aluminum as the metal matrix with 99.7% purity and 03≥ μm particle size reinforced with alumina (Al2O) 99.7% purity with 53 μm in size and Silicon Carbide (SiC) 99.7% purity with 95 ≥ μm in size to prepare the (Al – 10wt% Al3–20wt%SiC) composite, these  omposites were cold pressed through uniaxial pressing at different pressure of (500,600,700,800,900)MPa and sintered at 5500C for one hour. The composite products were treated thermally using both rapid isothermal heating and traditional heating at temperature 400oC for 15min and then cooled in steady air. The research aims to study the effect of pressing pressure, heat treatments on the properties of the samples since it was found that the physical properties (density, porosity and thermal conductivity) increases with increasing pressing pressure and increase significantly after heat treatment (rapid isothermal heating and traditional heating) was accompanied by an increase in the mechanical properties (hardness, compressive strength).

Download Full-text PDF

Keywords: Powder metallurgy technique, pressing pressure, heat treatment; Al –10 wt% Al2O3– 20wt%Sic.

How to cite

TJES: Razooqi RN, Abtan NS, Hamood HS. The effect of heat treatment on the composite properties based on aluminum and reinforcement alumina and silicon carbide prepared by powder metallurgy technique. Tikrit Journal of Engineering Sciences 2017; 24 (4): 1-8.
APA:  Razooqi,  R. N., Abtan,  N.S. & Hamood,  H. S.  (2017). The effect of heat treatment on the composite properties based on aluminum and reinforcement alumina and silicon carbide prepared by powder metallurgy technique. Tikrit Journal of Engineering Sciences, 24(3), 1-8.